Telcar® TL-1000-105
注： 该材料由 TEKNOR APEX 厂家直供，厂家技术人员进行生产指导，提供正规出场报告，相关检测报告等。
| 种类 : | TPE |
| 品牌 : | Telcar® |
| 用途 : | 通用、工业应用 |
Telcar® TL-1000-105 原厂PDF物性资料.pdf 
订购热线：021-58958519 13061808058(赵先生)
Telcar® TL-1000-105 产品信息
| 基本信息 | |
|---|---|
| 黄卡编号 |
|
| 特性 |
|
| 用途 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.890 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D, 5 秒) | 59 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 弯曲模量 | 655 | MPa | ASTM D790 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 | ASTM D412 | ||
| 横向流量 : 100%应变 | 11.0 | MPa | ASTM D412 |
| 流量 : 100%应变 | 13.1 | MPa | ASTM D412 |
| 抗张强度 | ASTM D412 | ||
| 横向流量 : 断裂 | 13.4 | MPa | ASTM D412 |
| 流量 : 断裂 | 15.9 | MPa | ASTM D412 |
| 伸长率 | ASTM D412 | ||
| 横向流量 : 断裂 | 290 | % | ASTM D412 |
| 流量 : 断裂 | 230 | % | ASTM D412 |
| 撕裂强度 - 横向流量 1 | 121 | kN/m | ASTM D624 |
| 压缩永久变形 | ASTM D395 | ||
| 23°C, 22 hr | 54 | % | ASTM D395 |
| 70°C, 22 hr | 74 | % | ASTM D395 |
| 90°C, 70 hr | 93 | % | ASTM D395 |
| 老化 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 空气中拉伸强度的变化率 | ISO 188 | ||
| 110°C, 1008 hr | 3.4 | % | ISO 188 |
| 125°C, 168 hr | 1.8 | % | ISO 188 |
| 在空气中断裂时拉伸应力变化 | ISO 188 | ||
| 110°C, 1008 hr | -34 | % | ISO 188 |
| 125°C, 168 hr | -19 | % | ISO 188 |
| 空气中邵氏硬度的变化率 (支撐 D, 110°C, 1008 hr) | 3.2 | ISO 188 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 脆化温度 | -55.0 | °C | ASTM D746 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| 可燃性 | 额定值 | 测试方法 | |
|---|---|---|---|
| UL 阻燃等级 (0.750 mm, All Colors) | HB | UL 94 |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 表观粘度 (200°C, 206 sec^-1) | 378 | Pa·s | ASTM D3835 |
| 法律声明 |
|---|
| The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries. |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 料筒后部温度 | 171 到 193 | °C | |
| 料筒中部温度 | 177 到 199 | °C | |
| 料筒前部温度 | 182 到 204 | °C | |
| 射嘴温度 | 188 到 210 | °C | |
| 加工（熔体）温度 | 188 到 210 | °C | |
| 模具温度 | 25.0 到 65.6 | °C | |
| 注塑压力 | 1.38 到 6.89 | MPa | |
| 注射速度 | 中等偏快 | ||
| 背压 | 0.172 到 0.345 | MPa | |
| 螺杆转速 | 50 到 100 | rpm | |
| 垫层 | 3.81 到 25.4 | mm |
| 注射说明 |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 80.0 | °C | |
| 干燥时间 | 2.0 | hr | |
| 料筒1区温度 | 166 到 188 | °C | |
| 料筒2区温度 | 171 到 193 | °C | |
| 料筒3区温度 | 177 到 199 | °C | |
| 料筒5区温度 | 182 到 204 | °C | |
| 口模温度 | 190 到 210 | °C |
| 挤压说明 |
|---|
| 螺杆转速30 - 100 rpm |
| 备注 | |
|---|---|
| 1 . | C 模具 |