Sarlink® TPE FM-2676 (PRELIMINARY DATA)
注： 该材料由 TEKNOR APEX 厂家直供，厂家技术人员进行生产指导，提供正规出场报告，相关检测报告等。
| 种类 : | TPE |
| 品牌 : | Sarlink® TPE |
| 用途 : | 汽车内部零件、汽车领域的应用、橡胶取代、Thermoforming Applications |
Sarlink® TPE FM-2676 (PRELIMINARY DATA) 原厂PDF物性资料.pdf 
订购热线：021-58958519 13061808058(赵先生)
Sarlink® TPE FM-2676 (PRELIMINARY DATA) 产品信息
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.10 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 | ISO 868 | ||
| 邵氏 A, 1 秒, 注塑 | 79 | ISO 868 | |
| 邵氏 A, 5 秒, 注塑 | 77 | ISO 868 | |
| 邵氏 A, 15 秒, 注塑 | 75 | ISO 868 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 1 | ISO 37 | ||
| 横向流量 : 100%应变 | 2.53 | MPa | ISO 37 |
| 流量 : 100%应变 | 3.75 | MPa | ISO 37 |
| 拉伸应力 2 | ISO 37 | ||
| 横向流量 : 断裂 | 9.20 | MPa | ISO 37 |
| 流量 : 断裂 | 6.30 | MPa | ISO 37 |
| 伸长率 3 | ISO 37 | ||
| 横向流量 : 断裂 | 970 | % | ISO 37 |
| 流量 : 断裂 | 460 | % | ISO 37 |
| 撕裂强度 4 | ISO 34-1 | ||
| 横向流量 | 46 | kN/m | ISO 34-1 |
| 流量 | 44 | kN/m | ISO 34-1 |
| 压缩永久变形 5 | ISO 815 | ||
| 23°C, 22 hr | 22 | % | ISO 815 |
| 70°C, 22 hr | 37 | % | ISO 815 |
| 90°C, 70 hr | 61 | % | ISO 815 |
| 老化 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 空气中拉伸强度的变化率 6 | ISO 188 | ||
| 横向流量 : 110°C, 1008 hr | -1.9 | % | ISO 188 |
| 流量 : 110°C, 1008 hr | 10 | % | ISO 188 |
| 横向流量 : 100% 应变 110°C, 1008 hr | 13 | % | ISO 188 |
| 流量 : 100% 应变 110°C, 1008 hr | -2.6 | % | ISO 188 |
| 在空气中断裂时拉伸应力变化 7 | ISO 188 | ||
| 横向流量 : 110°C, 1008 hr | -3.5 | % | ISO 188 |
| 流量 : 110°C, 1008 hr | 14 | % | ISO 188 |
| 空气中邵氏硬度的变化率 | |||
| 邵氏 A, 110°C, 1008 hr 8 | -0.40 | ISO 188 | |
| 邵氏 A, 110°C, 1008 hr 9 | -0.50 | ISO 188 |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 表观粘度 (200°C, 206 sec^-1) | 617 | Pa·s | ASTM D3835 |
| 法律声明 |
|---|
| The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries. |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 料筒后部温度 | 227 到 249 | °C | |
| 料筒中部温度 | 227 到 249 | °C | |
| 料筒前部温度 | 227 到 249 | °C | |
| 射嘴温度 | 227 到 249 | °C | |
| 加工（熔体）温度 | 227 到 249 | °C | |
| 模具温度 | 16 到 32 | °C | |
| 注塑压力 | 1.38 到 6.89 | MPa | |
| 注射速度 | 快速 | ||
| 背压 | 0.172 到 0.862 | MPa | |
| 螺杆转速 | 50 到 120 | rpm | |
| 垫层 | 3.81 到 25.4 | mm |
| 注射说明 |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 料筒1区温度 | 216 到 238 | °C | |
| 料筒2区温度 | 216 到 238 | °C | |
| 料筒3区温度 | 216 到 238 | °C | |
| 料筒4区温度 | 216 到 238 | °C | |
| 料筒5区温度 | 216 到 238 | °C | |
| 口模温度 | 216 到 238 | °C |
| 挤压说明 |
|---|
| Screw Speed: 30 to 100 rpm |
| 备注 | |
|---|---|
| 1 . | 类型 1, 510 mm/min |
| 2 . | 类型 1, 510 mm/min |
| 3 . | 类型 1, 510 mm/min |
| 4 . | B 方法，直角形试样（不割口）, 510 mm/min |
| 5 . | 类型 A |
| 6 . | 类型 1 |
| 7 . | 类型 1 |
| 8 . | 1 sec |
| 9 . | 15 sec |