Chemlon® E-66 GF30

注：该材料由 TEKNOR APEX 厂家直供，厂家技术人员进行生产指导，提供正规出场报告，相关检测报告等。

种类 :	PA66
品牌 :	Chemlon®
用途 :

Chemlon® E-66 GF30 原厂PDF物性资料.pdf

订购热线：021-58958519 13061808058(赵先生)

Chemlon® E-66 GF30 产品信息

基本信息
填料/增强材料	玻璃纤维增强材料, 30% 填料按重量
外观	黑色自然色
加工方法	注射成型

物理性能	额定值	单位制	测试方法
密度	1.37	g/cm³	ISO 1183
收缩率 ¹	0.30 到 0.70	%	内部方法
吸水率 (平衡, 23°C, 50% RH)	1.8	%	ISO 62

机械性能	额定值	单位制	测试方法
拉伸模量	8000	MPa	ISO 527-2
拉伸应力 (断裂)	165	MPa	ISO 527-2
拉伸应变 (断裂)	3.0	%	ISO 527-2
弯曲模量	7000	MPa	ISO 178
弯曲应力 ²	195	MPa	ISO 178

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度	7.0	kJ/m²	ISO 180

热性能	额定值	单位制	测试方法
热变形温度
0.45 MPa, 未退火	> 240	°C	ISO 75-2/B
1.8 MPa, 未退火	230	°C	ISO 75-2/A

注射	额定值	单位制
干燥温度	80.0	°C
干燥时间	2.0	hr
料筒后部温度	275 到 300	°C
料筒中部温度	275 到 300	°C
料筒前部温度	275 到 300	°C
加工（熔体）温度	< 300	°C
模具温度	80.0 到 90.0	°C
注射速度	快速
螺杆转速	50 到 200	rpm

注射说明
Back pressure: LowInjection pressure: HighThe material is supplied dry and ready to mould in sealed, moisture proof sacks. No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present. Should drying become necessary, two hours at 80°C in a dehumidifying drier is recommended. The use of air circulating driers is not generally recommended, as longer drying times are often required, with greater potential for product oxidation and yellowing. Drying temperatures should not exceed 80°C.

注射说明

Back pressure: LowInjection pressure: HighThe material is supplied dry and ready to mould in sealed, moisture proof sacks. No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present. Should drying become necessary, two hours at 80°C in a dehumidifying drier is recommended. The use of air circulating driers is not generally recommended, as longer drying times are often required, with greater potential for product oxidation and yellowing. Drying temperatures should not exceed 80°C.

备注
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).
2 .	At Break

备注

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

2 .

At Break